I've been welding Aerospace since the '80s and I finally bought me the furick cup and tried it for the first time on inconel 718 and when I set the flowmeter to the recommended 20-30 it just didn't seem like it was enough so I cranked it to 50 and what a huge difference it made my inco look nice and...

Thank you Oscar,
This is true. I weld beer cans together with my 350. I was just curious and always willing to learn more about advanced settings. I do have one more question that maybe you could answer? On the Everlast set on 30%balance what is that on a dynasty?

Thank you for the clarification. That's a bummer the 350 doesn't have that option. I was told the 400 has it. I'd like to know how much of a difference there is by changing the waveform on the polarity sides? Hopefully that will be answered and another video.

Thanks for the quick response. In the video he described using the Miller dynasty 280 with the expansion card. He did not mention any other machine.So you're telling me these machines that you're displaying have that capability?

How? Postby Spweld » Wed Jul 29, 2020 3:37 pm I'm sorry I guess you don't understand my question Mike stated that you could put on the EN side a tri-wave setting and have a advanced Wave on the EP but that is not possible yes you can change your waveform but you cannot individually change your wavef...

I'm sorry I guess you don't understand my question Mike stated that you could put on the EN side a tri-wave setting and have a advanced Wave on the EP but that is not possible yes you can change your waveform but you cannot individually change your waveform as he indicated in the video. This is why ...

Hey Jody, You had a video with Mike z about welding the aluminum frames for bikes and he mentioned under the advanced settings to put the electrode negative in a triwave form and put the electrode positive on the advanced waveform and that is not possible to do. So I'd like to know how he was able t...

Hello Bjames, If you're doing aluminum you cannot go wrong with the dynasty buy Miller. But that mainly depends on the thickness of the materials you're welding especially if you're doing Aerospace welding you want a machine that is going to start at 3 amps and terminates the weld at 3 amps.Although...

I watched the video of The aluminum bike TIG welding and you started talking about the advanced settings and Mike mentioned he can change the waveform individually on the EN and EP. How can I do that on my 350 dynasty? Or does the 350 need an expansion card for that like the 280?

Thank you I read the entire file and there's no mention of interpass temperature and ranges. Although I did find some literature that stated to let it cool till it reaches 150 degrees before you can start your second pass. It's been 8 years since the last time I had to worry about that but on this j...

After welding your first pass welding stainless sockets elbows and flanges I know that there's a temperature range before you can weld your second pass so my question is at what temperature is it safe to weld my second pass?