Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
noddybrian
- noddybrian
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 24, 2013 12:13 pm
We must have posted almost together with similar thoughts - having looked again I would look at torch angle / gas flow / argon dam first while trying to not overheat of boil a large base metal puddle prior to adding filler - only try the 309 filler after ruling out gas issues as brand new horseshoes should weld with regular cheap ER70 rod - remember with Tig it's only the silicon / deoxidizers in the filler that can clean up impurities otherwise the longer & hotter you heat the base metal the more likely crap will boil out - other than appearance or less post weld clean up really Mig is more often used for this type work & usually welds fine - use nice small diameter wire fairly hot to achieve smooth but not too big welds.
I tried lowering my gas flow to 15 CFH. Also used 308 stainless filler road. Raised the amps to 173. I forgot to make a dam to coral the gas, but I'll try that next time. See Photo.
- Attachments
-
- IMG_7122.JPG (51.02 KiB) Viewed 4036 times
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
Better but you need to build a dam behind your weld area, I really believe you are drawing in air. Turn your gas down more. I have gone as low as 7 CFH. Too much flow causes a vortex and draws in air around something so small. You also need to pause a second to get a puddle, dip your filler and then repeat. It looks like you're lay wiring which cools off your puddle. Tig welds are flatter than other weld processes and filets can be somewhat concave.
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
If those were close up pics then those horseshoes look borderline on cast. I'm still thinking metal quality. I've welded on old pipe in buildings that were over 100 years old and you fight the same problems there. Holes sometimes and good welds 1/2 inch later.
I have more questions than answers
Josh
Josh
Ok. I'll try lowering the gas. I'll also try to reach out to the ebayer I bought them from to see if they are cast or not. Thanks guys. Just remembered. While welding I see sparks flying around the weld. Maybe impurities.
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
I suspect a technique issue. It may be as simple as you created mill scale on the backside and when you went to weld it you did not compensate for it. I find more heat faster, and getting some rod in right away for the "cleaning effect" works.donzi426 wrote:Just contacted ebayer about horseshoes. He said that "they are steel sand blasted. Great for welding, used on horses or other projects. "
I welded some heavily mill scaled flat stock to solid square stock that didn't have the mill scale removed because it would ruin the "rustic look."
I used 200+ amps and 3/32" rod. I went immediate full pedal to puddle quick and got rod in immediately - it all welded real nice and no grinder marks.
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
I'm in the "metal quality" camp on this, especially after the comment about sparks around the weld.
Higher quality shoes are available, but to work what you have, the fix is simple. Weld, grind, weld again. (Only where needed, of course.) You can grind about half the depth where it's porous, and re-weld.
I also recommend 309 for filler in all passes, because it resists porosity in poorer quality base metals, and this application is non-critical.
Steve S
Higher quality shoes are available, but to work what you have, the fix is simple. Weld, grind, weld again. (Only where needed, of course.) You can grind about half the depth where it's porous, and re-weld.
I also recommend 309 for filler in all passes, because it resists porosity in poorer quality base metals, and this application is non-critical.
Steve S
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
ER70 S6 is supposed to be good for dirty metal too. I am staying in the gas-issue, laywire cold puddle camp. I have never seen sparks come from anything other than trying to weld over millscale and OP says the shoes are sand blasted. I have had similar issues welding railroad spikes but they are soaked with creosote so trouble is expected but brand new horseshoes? Modern horseshoes would have to be, at least, a half-way decent alloy.
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
I agree with 309. I've used it on horseshoes too and it welds very niceOtto Nobedder wrote:I'm in the "metal quality" camp on this, especially after the comment about sparks around the weld.
Higher quality shoes are available, but to work what you have, the fix is simple. Weld, grind, weld again. (Only where needed, of course.) You can grind about half the depth where it's porous, and re-weld.
I also recommend 309 for filler in all passes, because it resists porosity in poorer quality base metals, and this application is non-critical.
Steve S
I've never had to grind welds on bulk ordered new horseshoes so something other than metal may be wrong?
Or maybe I've just been lucky
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
That's why I am staying in the camp I am in. Horseshoes can't be brittle so they can't be cast iron but I bet they are forged steel and it should weld just fine. Farriers still have to heat and custom fit pre-made shoes because you can't take your horse to Shoe Carnival and let him try them on so I am betting its a torch nut error.MinnesotaDave wrote:I agree with 309. I've used it on horseshoes too and it welds very niceOtto Nobedder wrote:I'm in the "metal quality" camp on this, especially after the comment about sparks around the weld.
Higher quality shoes are available, but to work what you have, the fix is simple. Weld, grind, weld again. (Only where needed, of course.) You can grind about half the depth where it's porous, and re-weld.
I also recommend 309 for filler in all passes, because it resists porosity in poorer quality base metals, and this application is non-critical.
Steve S
I've never had to grind welds on bulk ordered new horseshoes so something other than metal may be wrong?
Or maybe I've just been lucky
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
They very well could be some kind of cast steel or pig iron. Forged in outer china from old tin army badges and medals. Shipped over in an open wood crate on the deck of a ship. Rusted for months in a ship yard then sand blasted and sold on the cheap. Looking at the closeup pick you can see it has a poor quality to the metal that looks more than surface deep. Perfect for art. But probably looked over or tossed out by the ferrier.
I have more questions than answers
Josh
Josh
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
You're probably right. If it was me...I would just Silbr the things and be done with it. I think the nice gold color would make it look cool. I can't believe we spent 4 pages fighting over horseshoes...oh wait...yes I canPoland308 wrote:They very well could be some kind of cast steel or pig iron. Forged in outer china from old tin army badges and medals. Shipped over in an open wood crate on the deck of a ship. Rusted for months in a ship yard then sand blasted and sold on the cheap. Looking at the closeup pick you can see it has a poor quality to the metal that looks more than surface deep. Perfect for art. But probably looked over or tossed out by the ferrier.
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
I was starting to consider metal being the problem except for exnailpounder claiming "torch nut error."
Now that's my favorite reason because it makes me laugh and I no longer want to consider metal as the problem.
Now that's my favorite reason because it makes me laugh and I no longer want to consider metal as the problem.
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Today I tried something and I believe it works. Didn't clean or sand the horseshoes. Raised the heat to 180 Amps. Raised the gas flow to 20 CFH (lowering it just caused a mess). Used 70R-6 filler rod. Concentrated on the arc angle and bingo. Pretty nice weld. The second side wasn't as pretty, but I think by doing the first side it must release some of the contaminants in these shoes. See photos. I want to thank everyone who contributed to my post. Those suggestions did help.
- Attachments
-
- IMG_7126.JPG (51.45 KiB) Viewed 1970 times
Last edited by donzi426 on Sat Mar 04, 2017 5:06 pm, edited 1 time in total.
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
You did not form a proper puddle on both pieces - if you look at the toes of your first pic you can see a distinct lack of fusion.donzi426 wrote:Today I tried something and I believe it works. Didn't clean or sand the horseshoes. Raised the heat to 180 Amps. Raised the gas flow to 20 CFH (lowering it just caused a mess). Used 70R-6 filler rod. Concentrated on the arc angle and bingo. Pretty nice weld. The second side wasn't as pretty, but I think by doing the first side it must release some of the contaminants in these shoes. See photos. I want to thank everyone who contributed to my post. Those suggestions did help.
Maybe you should practice fillets on regular T joints and show them for some tips on tigging them?
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
[quote="donzi426"]You're right Dave. I do need more practice on fillets. Back to the drawing board:-)[/quote Or use mig. Mig works on anything. Once you paint your project, a couple of iffy welds won't matter to anyone other than another welder looking to start some shit
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
I love it you can disagree totally about something on one thread and yet pat someone on the back two posts later. Lots of times I will argue a point until I totally understand I'm wrong and then turn 180 deg and run just as hard the other way.
I have more questions than answers
Josh
Josh
Return to “Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources