I apologize for my pissing contest. Here's some pics and settings and techniques I used today that should help for 16 gauge also however you'll need more amperage.
This is all 22 gauge stainless. No backing no chill blocks no purge.
This is the tack move to the edge of the puddle and tack method. With no filler. I make a tack step off the pedal move forward and hit the pedal again, it's an easy way to control heat input.
35 amps maybe? Can't remember anymore.
Pulse at 10 background 10 on time 30ish amps 5-7 seconds pulse and a very fast pace.
This is with 1/16" filler. Same method I used before I tack and add a small amount of filler let off the pedal move forward and tack and add filler again. Very simple and effective just slow.
Tack move tack method
Just remember fit up is key especially with fusion welds.
More of the tack move tack method.
Anyways I apologize and I hope this helps. I'm not posting these for any other reason then to help.
Your well on your way already and since you have chill blocks that will help a lot.
Sent from my SM-G920V using Tapatalk
Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
The piece I will be welding is going to have a continuous weld that will be 19" vertically. Obviously I plan to tac a lot but I was wondering if I should alternate my welds on each side until they meet in the center? So I would weld say 3" on the top and then 3" on the bottom right away, wait for them to cool then repeat until they meet. Or will I be ok if I just take my time for cooling and just run right up bottom to top?
Is it possible to orient the pieces horizontally while you weld them? If so, you will not have to battle the heat so much and you should get a more consistent weld. 19" is pretty long in my opinion but you can if the heat control is right. If it were me, I'd start in the middle and weld to the corners splitting it into 2 beads. That can give you a nice tie-in and change the bead directions. (Flip the piece end-for-end so you are welding in the same direction physically).
- LtBadd
-
Weldmonger
-
Posts:
-
Joined:Sun Apr 12, 2015 4:00 pm
-
Location:Clearwater FL
-
Contact:
The only thing about this is the crater (or butt hole) that is left when you snap off the pedal, I personally wouldn't like that and the method seems to be slow, more then one way to get the job done and each of us might approach this differently, and that's a good thing about learning what technique others use.5th Street Fab wrote: This is all 22 gauge stainless. No backing no chill blocks no purge.
This is the tack move to the edge of the puddle and tack method. With no filler. I make a tack step off the pedal move forward and hit the pedal again, it's an easy way to control heat input.
35 amps maybe? Can't remember anymore.
Richard
Website
Website
- 5th Street Fab
-
Guide
-
Posts:
-
Joined:Sun Jan 15, 2017 1:08 am
Agreed it is very slow and no one likes craters. But it's just another way to get pretty colors with none of the fancy stuff (big cups and chill blocks).LtBadd wrote:The only thing about this is the crater (or butt hole) that is left when you snap off the pedal, I personally wouldn't like that and the method seems to be slow, more then one way to get the job done and each of us might approach this differently, and that's a good thing about learning what technique others use.5th Street Fab wrote: This is all 22 gauge stainless. No backing no chill blocks no purge.
This is the tack move to the edge of the puddle and tack method. With no filler. I make a tack step off the pedal move forward and hit the pedal again, it's an easy way to control heat input.
35 amps maybe? Can't remember anymore.
Here's the same technique but dabbing with 040 filler
And for thin stainless I use .040 tungsten it's just what I learned on so I'm used to it. It's easy to start at low amperage.
Sent from my SM-G920V using Tapatalk
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
- 20170311_123635.jpg (45.35 KiB) Viewed 888 times
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
- 20170311_155646.jpg (45.4 KiB) Viewed 874 times
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
I started welding it today and well one of the pieces is 1/16" off so I can't do an autogenous weld on one end. I had to bridge the two sides and add some filler where it was off but that put a lot of heat in and lost the color for 2". Btw I am welding in the flat. It does not look great for what I wanted but if I have to wire brush it then that will be the new look.
- Attachments
-
- 20170312_041305.jpg (28.52 KiB) Viewed 845 times
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
You can always wire-brush it (a clean brass brush will take the color off without scratching the surface), then bring the color back by welding back over it, no filler, with just enough heat to form a shallow puddle. Using pulse if you have it, or a step-pause motion will keep the stack-of-dimes look. Use the chill block again to avoid adding distortion.
On the other hand, It'll look good brushed, too.
Steve S
On the other hand, It'll look good brushed, too.
Steve S
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
First fit up. The welds just look brown from a far so they will be brushed and then I hope to get a nice reflective finish after this.... Pretty ugly for people who don't like welding.
- Attachments
-
- 20170312_205540.jpg (57.06 KiB) Viewed 818 times
exnailpounder
- exnailpounder
-
Weldmonger
-
Posts:
-
Joined:Thu Dec 25, 2014 9:25 am
-
Location:near Chicago
Try a little powdered Barkeepers Friend. It will take the color out back to a natural stainless look and will also take out the HAZ colors without scratching. Don't use a scrubby, just a rag or paper towel. Works great.
Ifyoucantellmewhatthissaysiwillbuyyouabeer.
I was so wrapped up in reading your thread, I never stopped to think about what you were making exactly. I am dubious that choosing stainless was a good idea for your case. Stainless has pretty bad thermal properties in terms of dispersing its heat. So all the heat generated internally by your components, will stay confined within this case, and the case will get hot and trap the heat.
These are very bad situations for a computer. Perhaps you have considered this already and have a water-cooled solution planned, or other type of auxiliary cooling, but internal fans will not solve this issue. Just putting that out there-
These are very bad situations for a computer. Perhaps you have considered this already and have a water-cooled solution planned, or other type of auxiliary cooling, but internal fans will not solve this issue. Just putting that out there-
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
cj737 wrote:I was so wrapped up in reading your thread, I never stopped to think about what you were making exactly. I am dubious that choosing stainless was a good idea for your case. Stainless has pretty bad thermal properties in terms of dispersing its heat. So all the heat generated internally by your components, will stay confined within this case, and the case will get hot and trap the heat.
These are very bad situations for a computer. Perhaps you have considered this already and have a water-cooled solution planned, or other type of auxiliary cooling, but internal fans will not solve this issue. Just putting that out there-
That's what I am testing now. The front of the case has a 1" gap between the chassis and the stainless where there is a 200mm fan with a duct that takes in air. The top and bottom of the front stainless are open. The 1" black cap ontop is actually hollow and has vents And the rear of the case is open with exhaust fans. I don't have liquid cooling because the case was already operating 10- 15 degrees c below the standard temp for my 8core amd cpu. Also my gtx 1070 is helped by a pivoting 140mm fan for exhaust mid case. I have a monitor on it for now. I will run it for a day and compare temps.
- Attachments
-
- 20170315_021013.jpg (52.42 KiB) Viewed 1105 times
Well at least your welds are looking lovely I hope it works out for you. If not, switch to aluminum; its a better material for what you're after.
Something else you do possibly do is to drill/punch holes in the side panels to increase the venting especially since you have a motorized fan in there. And free air space around, below and above that case to provide cool air flow is pretty important.
Best of luck, its looking really cool!
Something else you do possibly do is to drill/punch holes in the side panels to increase the venting especially since you have a motorized fan in there. And free air space around, below and above that case to provide cool air flow is pretty important.
Best of luck, its looking really cool!
just browsed through all the replies and everything seems covered, so sorry if I repeat anything... most of all the work I do on the job is stainless, and corner welds are pretty simple... 16 gauge is pretty thick stuff so it should be a breeze to do. The key in my job is to get lots and lots of tacks... and then just fusion weld it, no need for filler. Just set it a little hot and move quick, never hang around, just enough to fuse it... If it was thin stuff like 20 gauge I would say stick an piece of aluminum behind it for a dam, but 16 won't need it...
can't believe it took me this many years to buy a diamond wheel for my bench grinder... what a difference
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
Thankscj737 wrote:Well at least your welds are looking lovely I hope it works out for you. If not, switch to aluminum; its a better material for what you're after.
Something else you do possibly do is to drill/punch holes in the side panels to increase the venting especially since you have a motorized fan in there. And free air space around, below and above that case to provide cool air flow is pretty important.
Best of luck, its looking really cool!
I would love to have done this with aluminum but every encounter I have with aluminum has been rough. I have a 6x5 sheet of aluminum diamond plate I could have used but It was passed my skill level. I need to get more time to learn how to properly prep aluminum and fine tune my machine and I need to play around a bit but all my scrap is mostly mild steel and stainless.
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
Airflow test and fitting are finished all that's left is to clean up and set up some kind of latch instead of screwing into the case.
- Attachments
-
- 20170315_031317.jpg (34.58 KiB) Viewed 1036 times
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
Yea they are awesome. I actually have one of the tools at home that I used for the cycling industry. The problem is where the door hits the case it's completely flush and if I place it there it will stick up a bit.cj737 wrote:Have you ever tried "rivet nuts"? They work exceptionally well on sheet material. You can get them in small metric or SAE sizes and then choose a fastener head type (like stainless button head torx) that suits your fancy.
- WoodpeckerWelder
-
Workhorse
-
Posts:
-
Joined:Sun Feb 12, 2017 1:08 am
-
Location:N Georgia USA
Any chance of recessing a tab to mount the nut to?408cheytac wrote:Yea they are awesome. I actually have one of the tools at home that I used for the cycling industry. The problem is where the door hits the case it's completely flush and if I place it there it will stick up a bit.cj737 wrote:Have you ever tried "rivet nuts"? They work exceptionally well on sheet material. You can get them in small metric or SAE sizes and then choose a fastener head type (like stainless button head torx) that suits your fancy.
"Why is there never time to do anything right the first time but always time to do it again?"
You know there are a "flared" version of them? They are easy to recess.408cheytac wrote:The problem is where the door hits the case it's completely flush and if I place it there it will stick up a bit.
You just need to drill and counter-sink a hole and just press down a screw. If you can't use a press or the bench vise just put a nut behind and tighten. 16 gauge SS might need some heat though.
Tools for the riv-nut can easily be made too. The threads in the long nut has been drilled out. Just hold the stem steady and tighten the small nut and its done deal.
- IMG_20170317_33627.jpg (53.13 KiB) Viewed 898 times
Pictures from my scrap collection:
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
408cheytac
- 408cheytac
-
New Member
-
Posts:
-
Joined:Tue May 26, 2015 12:06 am
-
Location:Philadelphia
I didn't think of that. I was a thinking of maybe a rivet looking piece like the ones where the bottom of the rivet head is a square. Right now I have it set up with just standard case screws. The one drawback of the case is that it's a bitch to take off.AndersK wrote:You know there are a "flared" version of them? They are easy to recess.408cheytac wrote:The problem is where the door hits the case it's completely flush and if I place it there it will stick up a bit.
You just need to drill and counter-sink a hole and just press down a screw. If you can't use a press or the bench vise just put a nut behind and tighten. 16 gauge SS might need some heat though.
Tools for the riv-nut can easily be made too. The threads in the long nut has been drilled out. Just hold the stem steady and tighten the small nut and its done deal.
The attachment IMG_20170317_33627.jpg is no longer available
Also here are some updated pictures.
- Attachments
-
- 20170318_030517.jpg (27.52 KiB) Viewed 881 times
- WoodpeckerWelder
-
Workhorse
-
Posts:
-
Joined:Sun Feb 12, 2017 1:08 am
-
Location:N Georgia USA
Looks most cool.....
"Why is there never time to do anything right the first time but always time to do it again?"
Return to “Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities