Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Anything from 1/4" and up will work. Get into the thick stuff, and you'll need to preheat the base material to get your first beads to flow (or use about 250amps!). The upside of using 1/2" is that it will withstand an enormous amount of practice beads before turning to goo-
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

That's a lot of work to get a bead at all. First a couple passes of just pushing a puddle then try to add some filler, then put that burning torch down.
Attachments
HalfInchPad.JPG
HalfInchPad.JPG (35.75 KiB) Viewed 1499 times
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Is this what you mean by goo? I was hoping to get another layer on this one.
Attachments
Goo.JPG
Goo.JPG (45.09 KiB) Viewed 1496 times
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Yup. And yup.

The trick with thick aluminum is that it takes an enormous amount of heat to get your first puddle. The base material keeps that heat for a LONG time, so you can run another few passes more easily. But, you need to quickly taper off the heat used to get your first puddle because the accumulated heat is melting the interior (below the oxide layer). Continuing to weld only turns the interior (melts at a much lower temp than the oxide) to goo so your puddle/beads are just rubbery snot worms.

You can plunge the part in a bucket of water to quickly quench it without losing all the heat. I like 1/4" for practice, not 1/2". 1/2" is (in my opinion) much harder to deal with for the reasons mentioned above.
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Practice lap #5 today.
Attachments
Lap7.23.JPG
Lap7.23.JPG (24.08 KiB) Viewed 1484 times
jroark
  • Posts:
  • Joined:
    Thu Jul 16, 2015 2:39 pm
  • Location:
    Ramseur, NC

I've also been practicing on some 1/8" and I have my machine set at 140A until I run a pass or two and then I cut it back to around 130A or so. Sometimes I'll run a bead a little cold just to see if I have enough control to keep from just flooring the pedal. I'm really just looking for consistent bead width and uniformity. I'm thinking that on the thinner stuff having more control of the pedal and being able to make consistent beads is more important than penetration. Not trying to say penetration isn't a very important factor either.
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

I had not tried a T joint lately and gave one a try with a #5 cup. I was impressed by how shiny the tungsten stayed.
Attachments
T.July26.JPG
T.July26.JPG (20.78 KiB) Viewed 1405 times
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Dip less, travel more. You'll continue to get smoother and more consistent beads :)
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Thank you.
Warrenh
  • Posts:
  • Joined:
    Thu Apr 27, 2017 12:31 pm

Gene, I'm wondering how you place your torch hand when you are welding. It looks like you might be having trouble moving it smoothly. Dont put too much pressure down on the table. Just lightly touch it with the heel of your hand. I sometimes extend my pinky and just touch the tip of the surface is rough or hard to slide on.

Sent from my SCH-I545 using Tapatalk
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Warren, Thank you too. I'm a leaner. I'll have to work on my posture to put less force on my torch hand.
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

I think I figured out what a contaminated weld puddle looks like. This would be tungsten contamination.
Attachments
ContaminatedPuddle.JPG
ContaminatedPuddle.JPG (35.32 KiB) Viewed 1326 times
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Learn something every time you weld!

I think it's tremendous that you're plowing away, working towards a goal, unafraid of public commentary. With that determination, IG will no doubt have a new, highly trafficked account 8-)
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Today's contaminated pool is a 309LW failure.
Attachments
Failure309LW.JPG
Failure309LW.JPG (33.44 KiB) Viewed 1307 times
Poland308
  • Posts:
  • Joined:
    Thu Sep 10, 2015 8:45 pm
  • Location:
    Iowa

Leaving the wire stuck in the puddle isn't contamination. It's something I do regularly. I use it as a location to taper of my arc as I reposition. Then I just light back up on the wire.
I have more questions than answers

Josh
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Yeah yeah That's what I meant.... I always do that on purpose. :lol:
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

And doing that also protects the filler wire from contamination from being exposed to the atmosphere. It's commonly intentional for stainless pipewelders to do this. Now, if it were your tungsten, that would be a different story... :o
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

That was the "W" in the failure mode. At one time I had 2 tungstens and a filler at the same time.
Gene.243
  • Posts:
  • Joined:
    Sat Sep 27, 2014 8:43 pm
  • Location:
    Southwest Oklahoma

Wow, what a break from the internet. I didn't mean to just disappear. I've been welding regularly just not getting online much. That broken chair that I was welding seems to have lost it's temper and now if you lean back too far it changes the neutral point where the rocking chair rocks. Oh well, it was broken before I tried to fix it.
Post Reply