Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
- weldin mike 27
-
Weldmonger
-
Posts:
-
Joined:Fri Apr 01, 2011 10:59 pm
-
Location:Australia; Victoria
Mick, Mike it's all good. The only tip I can give you not to be impatient. Do a few dabs and let it cool off. I am my own worst enemy when it comes to stuff like this as I don't wait long enough. Cooling off and using a wire brush on the repair as you go to get rid of the oxide scale. Don't be afraid to start half way across the joint, when starting a fresh one, the welding into the end of your bead. It'll give you a lump to land on and suck out a little heat. On thin work, a precisely sharpened and polished electrode will make a difference, and make it easier for you get the joint welded with out having to hang around. Also you may need to clean up the inside of the tubes as well, because the weld will draw crud from the underside
- weldin mike 27
-
Weldmonger
-
Posts:
-
Joined:Fri Apr 01, 2011 10:59 pm
-
Location:Australia; Victoria
Maybe a little thicker filler rod? Can help chill the puddle and give you a moment to get on with it
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
Alan,
Run bead after bead on a flat plate of 1/8" or thicker. Don't worry about joints yet, just practice getting a nice level and constant widths on your beads.
Just keep going, you got to put in a lot of helmet time. Looking good though.
Mark
Run bead after bead on a flat plate of 1/8" or thicker. Don't worry about joints yet, just practice getting a nice level and constant widths on your beads.
Just keep going, you got to put in a lot of helmet time. Looking good though.
Mark
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
I think you need to strait weld with no pulse (with your pedal or otherwise). Just to many things on your plate to begin with. Heck, after looking at my weld and it's all flat and almost melted through, I forget I have a pedal to control my amps. There's so much to think about in a very short time! It has to become second nature.
I love your spirit!
I love your spirit!
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
Your welds are looking better!!! Don't blame the steel, it just takes practice. I love your persistence!
Looking good.
Looking good.
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
Your welds show you're getting very comfortable with welding. It is now time to weld your cart together! Show us pics!
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
I think you're fighting your fit-up, more than running a bead. Advanced welders have no problem with gaps. For the beginner, they're just another headache to over come. Your pedal is your friend when it comes to gaps. I would like to see your joint before you start welding. How are you cutting your steel?
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
- tungstendipper
-
Weldmonger
-
Posts:
-
Joined:Sun Nov 19, 2017 10:09 am
You've had a tuff week of learning. Keep your chin up, move on, and ignore some. Just keep up the practice. It WILL get better.
Lincoln MP 210, Lincoln Square Wave 200,
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
Everlast 210 EXT
Thermal Dynamics 25 Plasma cutter
" Anything that carries your livelihood wants to be welded so that Thor can’t break it."
CJ737
I'll probably get flamed for this but I'm a manual pulse welder. I learned this way from a unbelievable welder/fabricator. Teaches control, allows you keep the heat out etc etc ......BUT.... Its kinda got its time and place. IMO for fusion welds it works great, I also seem to use this practice when welding aluminium for the most part. But when welding stainless unless it's a lap joint, I have found it will hinder your performance. Especially if welding pie cut tubing or well any butt joint.
I mostly am a member on a car forum, in the performance sections (turbos and shit). Have been for many many years. Sometimes we feel like broken records and may come off as asses sometimes. But, mostly its cause we have been there done that. A lot of those times it cost us valuable time and money. So, listening to knowledgeable guys that dedicate there time to participate on an internet forum should be greatly appreciated. This is how to get ahead of the game. Learn from those that have been there. There is much more knowledge to be had here, then BookFace , Instagram, Tinders or whatever. Those are where the You Tube Scholars hang out. Its easy to Google and type the "right" answer. But, its the tricks of the trade that you will learn from the hands on experienced. Having a "teacher" ready to respond to you at all hours of the day/night is priceless.. Don't knock it, embrace it.
/rant
Sent from my E6782 using Tapatalk
I mostly am a member on a car forum, in the performance sections (turbos and shit). Have been for many many years. Sometimes we feel like broken records and may come off as asses sometimes. But, mostly its cause we have been there done that. A lot of those times it cost us valuable time and money. So, listening to knowledgeable guys that dedicate there time to participate on an internet forum should be greatly appreciated. This is how to get ahead of the game. Learn from those that have been there. There is much more knowledge to be had here, then BookFace , Instagram, Tinders or whatever. Those are where the You Tube Scholars hang out. Its easy to Google and type the "right" answer. But, its the tricks of the trade that you will learn from the hands on experienced. Having a "teacher" ready to respond to you at all hours of the day/night is priceless.. Don't knock it, embrace it.
/rant
Sent from my E6782 using Tapatalk
I'm a mostly pedal pulser except for stainless. This is .083"4130 chromoly. The machine was set(if memory serves) to around 140 amps. Note the color and lack of HAZ. Anyone that tells you manually pulsing with the pedal increases heat is doing it wrong
- Attachments
-
- 20110314082249b.jpg (222 KiB) Viewed 959 times
Return to “Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities