Stick Welding Tips, Certification tests, machines, projects
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
An instructor from the local tech school came to our high school today and did some assessment and demonstrations and dripped off a bunch of stuff. Aluminum and steel drops, some tig filler, and a 25 lb box of 3/32" Excalibur 7018s. All we have at school is an old Airco AC buzzbox and I know it is possible to run 7018s on AC but I'm looking for tips. Any advice for running them on AC. Amps, technique, angle, anything at all will help
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
No student will ever go into the field and weld 7018 on AC. Yes, they make a so-called 7018AC rod, but it will not meet any code that will pay a welder real money.Farmwelding wrote:An instructor from the local tech school came to our high school today and did some assessment and demonstrations and dripped off a bunch of stuff. Aluminum and steel drops, some tig filler, and a 25 lb box of 3/32" Excalibur 7018s. All we have at school is an old Airco AC buzzbox and I know it is possible to run 7018s on AC but I'm looking for tips. Any advice for running them on AC. Amps, technique, angle, anything at all will help
This needs to be taught on a DC machine.
Steve S
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Yes I know and that was the first thing I told my teacher-we should get a DC stick machine. But that's bot going to happen unless I run the old Airco at 180 amps for 10 hours straight and then do that to the other old Airco. All I know is that we have 25 lb of them and they are all mine probably so any rod I can burn is helpful just to get the whole arc length and rod angle down.
Although it's funny... I don't know why but we probably have 20 lbs of 6010 electrodes in the back room and have always only had the Aircos. Fun fact-they don't run well on AC. That's what happens when I get bored I try new things just to get more hood time. I figure 25 lbs will keep me busy and out of my teachers hair
Although it's funny... I don't know why but we probably have 20 lbs of 6010 electrodes in the back room and have always only had the Aircos. Fun fact-they don't run well on AC. That's what happens when I get bored I try new things just to get more hood time. I figure 25 lbs will keep me busy and out of my teachers hair
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
Poleframer
- Poleframer
-
Workhorse
-
Posts:
-
Joined:Wed Feb 01, 2017 12:47 am
Hah, here's an opportunity to show you can do what it takes to get er done. Get some big diodes (only takes 4 of them), I got a box of them that would do, and make a bridge rectifier, like the one Jody has on the AC buzzbox in one of his vids, and walla...DC
REALLY isnt rocket science, and would be a good project if you can, then burn 7018 to your hearts desire.
Probably wouldnt have to do it in a real welding shop, but you gotta learn how to make the best of what ya have and show brain power, which is really what counts.
REALLY isnt rocket science, and would be a good project if you can, then burn 7018 to your hearts desire.
Probably wouldnt have to do it in a real welding shop, but you gotta learn how to make the best of what ya have and show brain power, which is really what counts.
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Nope... didnt go-our buzz box will not run them. Tried for a half an hour and nothing
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
Strange, I've run them on the cheap AC 225 Lincolns and a Century 225/125 buzz box (plus a couple others).Farmwelding wrote:Nope... didnt go-our buzz box will not run them. Tried for a half an hour and nothing
![Question :?:](./images/smilies/icon_question.gif)
They were a little harder to start and took a longer scratch than usual, went out now and then but overall ran OK.
Wouldn't want to do it all the time though.
One thing I noticed is that machines with a high/low tap needed to be on the low range side.
The low range side has higher OCV which translated into a higher welding voltage (7018 likes voltage
![Smile :)](./images/smilies/icon_e_smile.gif)
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Yeah, about an hour I posted that I thought about switching the leads since it has a low and high side. Ill give it a go here in another hour or so and try it.MinnesotaDave wrote:Strange, I've run them on the cheap AC 225 Lincolns and a Century 225/125 buzz box (plus a couple others).Farmwelding wrote:Nope... didnt go-our buzz box will not run them. Tried for a half an hour and nothing![]()
They were a little harder to start and took a longer scratch than usual, went out now and then but overall ran OK.
Wouldn't want to do it all the time though.
One thing I noticed is that machines with a high/low tap needed to be on the low range side.
The low range side has higher OCV which translated into a higher welding voltage (7018 likes voltage).
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
Interesting side note: In general with either AC or DC, when switched to high range, which is low OCV, the puddle behaves similar to when running an SA-200 on a higher coarse range/low fine.Farmwelding wrote:Yeah, about an hour I posted that I thought about switching the leads since it has a low and high side. Ill give it a go here in another hour or so and try it.MinnesotaDave wrote:
Strange, I've run them on the cheap AC 225 Lincolns and a Century 225/125 buzz box (plus a couple others).![]()
They were a little harder to start and took a longer scratch than usual, went out now and then but overall ran OK.
Wouldn't want to do it all the time though.
One thing I noticed is that machines with a high/low tap needed to be on the low range side.
The low range side has higher OCV which translated into a higher welding voltage (7018 likes voltage).
In general, 7018 does not prefer this setting on an SA-200, they like lower coarse range/high fine.
I've done this (used the high range) with Miller Dialarcs to make a 6010 vertical up puddle less fluid for a student.
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Just for you farmer.
I ran about 5# of 3/32 7018 DC and then 2# of 3/32 7018 AC. The arc force and amps all the same. I found the AC stuff to have a hard arc start.Compared to the D.C. Plus it seamed as though the weld was more like a 6013. It was spongy compared to other 7018 on D.C.
I ran about 5# of 3/32 7018 DC and then 2# of 3/32 7018 AC. The arc force and amps all the same. I found the AC stuff to have a hard arc start.Compared to the D.C. Plus it seamed as though the weld was more like a 6013. It was spongy compared to other 7018 on D.C.
I have more questions than answers
Josh
Josh
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
That's why I like this place.Poland308 wrote:Just for you farmer.
I ran about 5# of 3/32 7018 DC and then 2# of 3/32 7018 AC. The arc force and amps all the same. I found the AC stuff to have a hard arc start.Compared to the D.C. Plus it seamed as though the weld was more like a 6013. It was spongy compared to other 7018 on D.C.
Someone will take a minute to do the experiment, and report the results.
Steve S
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Well... Either way it wouldn't go in our machine for some reason. I used both the high and low side and changed the amps around and nothing went. So now all I have to do is hope we can get a DC stick welder.
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
Went out and made about 8 passes for you on AC.
1/8" 7018, old rod not in oven, welded fine from 135-150 amps AC.
135 amps for vertical up.
5/32" 7018, 150 amps AC.
Only real issue is getting it lit. Then you're golden.
"Pool cue" it for strike acuracy and to warm it up.
First welder I bought (1995) - after an oxy/acetylene that is.
Nothing special, about 8 passes, maybe more.
2 rod sizes, flat and vertical up.
1/8" 7018, old rod not in oven, welded fine from 135-150 amps AC.
135 amps for vertical up.
5/32" 7018, 150 amps AC.
Only real issue is getting it lit. Then you're golden.
"Pool cue" it for strike acuracy and to warm it up.
First welder I bought (1995) - after an oxy/acetylene that is.
- image.jpeg (45.82 KiB) Viewed 4242 times
2 rod sizes, flat and vertical up.
- image.jpeg (50.94 KiB) Viewed 4242 times
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
What do you mean pool cue the electrode. Never heard that term.MinnesotaDave wrote:Went out and made about 8 passes for you on AC.
1/8" 7018, old rod not in oven, welded fine from 135-150 amps AC.
135 amps for vertical up.
5/32" 7018, 150 amps AC.
Only real issue is getting it lit. Then you're golden.
"Pool cue" it for strike acuracy and to warm it up.
First welder I bought (1995) - after an oxy/acetylene that is.image.jpegNothing special, about 8 passes, maybe more.
2 rod sizes, flat and vertical up.image.jpeg
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
Pool cue means to hold the rod with your other hand down low near the steel.
Gives you fine motor control of the tip so you can control it precise enough to get those rods lit and warmed up on AC.
Otherwise they will often stick and not light.
Gives you fine motor control of the tip so you can control it precise enough to get those rods lit and warmed up on AC.
Otherwise they will often stick and not light.
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
That makes a lot more sense than what i thought it meant. Maybe will give it a go on Monday.MinnesotaDave wrote:Pool cue means to hold the rod with your other hand down low near the steel.
Gives you fine motor control of the tip so you can control it precise enough to get those rods lit and warmed up on AC.
Otherwise they will often stick and not light.
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
Just make sure you have a proper glove rated for stick on.Farmwelding wrote:. Maybe will give it a go on Monday.
Don't ask.....
![Wink ;)](./images/smilies/icon_e_wink.gif)
Pictures from my scrap collection:
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Don't worry I know why. I accidentally grabbed one somebody had just used for ab1/2" weld with my bare hand the other day and practically melted my hand off.AndersK wrote:Just make sure you have a proper glove rated for stick on.Farmwelding wrote:. Maybe will give it a go on Monday.
Don't ask.....
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
He he , no you don't
You can easily hold a used rod with a tig glove but don't pool cue with one. The radiation from the arc is strong enough to give blisters thru a tig glove without even touching any metal.![Mr. Green :mrgreen:](./images/smilies/icon_mrgreen.gif)
![Wink ;)](./images/smilies/icon_e_wink.gif)
You can easily hold a used rod with a tig glove but don't pool cue with one. The radiation from the arc is strong enough to give blisters thru a tig glove without even touching any metal.
![Mr. Green :mrgreen:](./images/smilies/icon_mrgreen.gif)
Pictures from my scrap collection:
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
http://forum.weldingtipsandtricks.com/v ... f=9&t=5677
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
Really he should only do this to get it started and warmed up, and then drop his hand back to the stinger in a few seconds.AndersK wrote:He he , no you don't![]()
You can easily hold a used rod with a tig glove but don't pool cue with one. The radiation from the arc is strong enough to give blisters thru a tig glove without even touching any metal.
The start can be really difficult with an AC buzz box.
The Century that I pictured starts them really good on DC in comparison.
If he masters arc starts on AC with that rod, he'll laugh at the simplicity of starting on DC
![Very Happy :D](./images/smilies/icon_e_biggrin.gif)
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Popeye the old miner
- Popeye the old miner
-
Workhorse
-
Posts:
-
Joined:Tue Mar 21, 2017 8:29 pm
-
Location:Pitman Pennsylvania
I did some work in an old coal breaker about 40 years ago, all they had was an old ac welder, I couldn't even guess who made it, someone said Westinghouse built it back in the 30s, but no one knew for sure as there was no tag of any kind on it. Anyway they busted the shaker frame, it was made out of heavy 8 inch c channel might have been 3/8 thick or better when it was new. They called me up to do it since I'm a skinny little shit and no one else could fit under the shaker. One thing about coal...it corrodes steel like crazy...sulfuric acid eats it up and what is left is very difficult to weld with a good machine let alone an old antique buzzer from the stone age. They said just get it together so it will run til Friday and we will replace it Saturday...bullshit...I know how miners are I am one, they will keep fixin it til there is more repair weld metal than original steel.
So I got the ol thing all lined up, dogged in place, grinded somewhat shiney and turned on the beast, crawled in side and under the shaker with a handful of 6011s and a handful of 7018s. Uriah the old bird who ran the shaker told me let me know where you want it set at I will turn it where you want it. Ok I said. I fussed a bit with some 1/8 inch 6011s til it ran good and got some steel into the shallow groove I cut with the grinder then slid out and did the same on the outside and on the flanges, then went down to the other end and repeated the process. Meanwhile I heard some smartass remarks we'll find out if this kid can weld, if he can with this ol beast we'll hire the little shit. Now one thing I learned a long time ago about 7018 rods...the next size smaller 7018 will run at just about the same setting as the larger 6011. So now I'm gonna burn 3/32 7018 over top of the 6011 root I didn't have much trouble getting it going, and I will admit I thought it was gonna be a fight but they lit up pretty quick, maybe it was the coal dirt on em who knows. Anyway it stayed together and eventually after 3 or 4 years after fixing various places on both sides of the shaker once a month or so we cut it up and built a whole new shaker water bay, got a new set of cams and bullrigged the whole damn thing in place.
Got hired on full time 2 days after that first repair and never looked back. Don't ever let anyone tell you that you cant do somethin, you never know until you try it for yourself
So I got the ol thing all lined up, dogged in place, grinded somewhat shiney and turned on the beast, crawled in side and under the shaker with a handful of 6011s and a handful of 7018s. Uriah the old bird who ran the shaker told me let me know where you want it set at I will turn it where you want it. Ok I said. I fussed a bit with some 1/8 inch 6011s til it ran good and got some steel into the shallow groove I cut with the grinder then slid out and did the same on the outside and on the flanges, then went down to the other end and repeated the process. Meanwhile I heard some smartass remarks we'll find out if this kid can weld, if he can with this ol beast we'll hire the little shit. Now one thing I learned a long time ago about 7018 rods...the next size smaller 7018 will run at just about the same setting as the larger 6011. So now I'm gonna burn 3/32 7018 over top of the 6011 root I didn't have much trouble getting it going, and I will admit I thought it was gonna be a fight but they lit up pretty quick, maybe it was the coal dirt on em who knows. Anyway it stayed together and eventually after 3 or 4 years after fixing various places on both sides of the shaker once a month or so we cut it up and built a whole new shaker water bay, got a new set of cams and bullrigged the whole damn thing in place.
Got hired on full time 2 days after that first repair and never looked back. Don't ever let anyone tell you that you cant do somethin, you never know until you try it for yourself
- Otto Nobedder
-
Weldmonger
-
Posts:
-
Joined:Thu Jan 06, 2011 11:40 pm
-
Location:Near New Orleans
I LIKE that story. I have a few like it, but not quite like it, in my history. The moral stands. It's not impossible because someone says so.Popeye the old miner wrote:I did some work in an old coal breaker about 40 years ago, all they had was an old ac welder, I couldn't even guess who made it, someone said Westinghouse built it back in the 30s, but no one knew for sure as there was no tag of any kind on it. Anyway they busted the shaker frame, it was made out of heavy 8 inch c channel might have been 3/8 thick or better when it was new. They called me up to do it since I'm a skinny little shit and no one else could fit under the shaker. One thing about coal...it corrodes steel like crazy...sulfuric acid eats it up and what is left is very difficult to weld with a good machine let alone an old antique buzzer from the stone age. They said just get it together so it will run til Friday and we will replace it Saturday...bullshit...I know how miners are I am one, they will keep fixin it til there is more repair weld metal than original steel.
So I got the ol thing all lined up, dogged in place, grinded somewhat shiney and turned on the beast, crawled in side and under the shaker with a handful of 6011s and a handful of 7018s. Uriah the old bird who ran the shaker told me let me know where you want it set at I will turn it where you want it. Ok I said. I fussed a bit with some 1/8 inch 6011s til it ran good and got some steel into the shallow groove I cut with the grinder then slid out and did the same on the outside and on the flanges, then went down to the other end and repeated the process. Meanwhile I heard some smartass remarks we'll find out if this kid can weld, if he can with this ol beast we'll hire the little shit. Now one thing I learned a long time ago about 7018 rods...the next size smaller 7018 will run at just about the same setting as the larger 6011. So now I'm gonna burn 3/32 7018 over top of the 6011 root I didn't have much trouble getting it going, and I will admit I thought it was gonna be a fight but they lit up pretty quick, maybe it was the coal dirt on em who knows. Anyway it stayed together and eventually after 3 or 4 years after fixing various places on both sides of the shaker once a month or so we cut it up and built a whole new shaker water bay, got a new set of cams and bullrigged the whole damn thing in place.
Got hired on full time 2 days after that first repair and never looked back. Don't ever let anyone tell you that you cant do somethin, you never know until you try it for yourself
Steve S
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
So I tried for another half an hour today and found out new combinations of swearing I have never heard. I had two and half actual beads today as well. The slag doesnt like coming off very well though. I am just going to hope and ray we get a DC stick machine sometime.
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
Oh and I noticed that the electrodes are actually 7018-1. Does this make a difference for what I'm trying to do?
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
- MinnesotaDave
-
Weldmonger
-
Posts:
-
Joined:Sun Oct 27, 2013 10:57 pm
-
Location:Big Lake/Monticello MN, U.S.A.
It does not, and what did you find when you looked up what the numbers and/or letters after the dash mean?Farmwelding wrote:Oh and I noticed that the electrodes are actually 7018-1. Does this make a difference for what I'm trying to do?
When I did the samples this weekend I noticed the slag would come off in large chunks, but not a full peel.
Otherwise it was about the same as normal for removal in the 135-150 amp AC range.
A little more spatter, louder, slightly unstable arc, but not too bad.
Dave J.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Beware of false knowledge; it is more dangerous than ignorance. ~George Bernard Shaw~
Syncro 350
Invertec v250-s
Thermal Arc 161 and 300
MM210
Dialarc
Tried being normal once, didn't take....I think it was a Tuesday.
Farmwelding
- Farmwelding
-
Weldmonger
-
Posts:
-
Joined:Thu Mar 10, 2016 11:37 pm
-
Location:Wisconsin
It appears that 7018-1 means that the weld is stronger at cold temperatures than a normal 7018.
Our buzz box only goes up to around 110-120 in the low range as you recommended but they are 3/32" so don't need that much anyways?
The lag on a t-joint i did required pounding and left a lot of white powder on the weld still and didn't want tor come off. The flat weld came off in small chunks as you said though. Ill keep working on it and when I get to use a 7018 on DC I'm sure I will be laughing at how easy it is. That's the way I usually learnt hings the quickest. DO it the hard way and then you'll appreciate things for what they are worth or never making the same mistake again. Stick before mig-oxy-fuel before tig. Helps put ting is perspective for me.
Our buzz box only goes up to around 110-120 in the low range as you recommended but they are 3/32" so don't need that much anyways?
The lag on a t-joint i did required pounding and left a lot of white powder on the weld still and didn't want tor come off. The flat weld came off in small chunks as you said though. Ill keep working on it and when I get to use a 7018 on DC I'm sure I will be laughing at how easy it is. That's the way I usually learnt hings the quickest. DO it the hard way and then you'll appreciate things for what they are worth or never making the same mistake again. Stick before mig-oxy-fuel before tig. Helps put ting is perspective for me.
A student now but really want to weld everyday. Want to learn everything about everything. Want to become a knower of all and master of none.
Instagram: @farmwelding
Nick
Instagram: @farmwelding
Nick
Return to “Stick Welding/Arc Welding - Shielded Metal Arc Welding”
Jump to
- Introductions & How to Use the Forum
- ↳ Welcome!
- ↳ Member Introductions
- ↳ How to Use the Forum
- ↳ Moderator Applications
- Welding Discussion
- ↳ Metal Cutting
- ↳ Tig Welding - Tig Welding Aluminum - Tig Welding Techniques - Aluminum Tig Welding
- ↳ Mig and Flux Core - gas metal arc welding & flux cored arc welding
- ↳ Stick Welding/Arc Welding - Shielded Metal Arc Welding
- ↳ Welding Forum General Shop Talk
- ↳ Welding Certification - Stick/Arc Welding, Tig Welding, Mig Welding Certification tests - Welding Tests of all kinds
- ↳ Welding Projects - Welding project Ideas - Welding project plans
- ↳ Product Reviews
- ↳ Fuel Gas Heating
- Welding Tips & Tricks
- ↳ Video Discussion
- ↳ Wish List
- Announcements & Feedback
- ↳ Forum News
- ↳ Suggestions, Feedback and Support
- Welding Marketplace
- ↳ Welding Jobs - Industrial Welding Jobs - Pipe Welding Jobs - Tig Welding Jobs
- ↳ Classifieds - Buy, Sell, Trade Used Welding Equipment
- Welding Resources
- ↳ Tradeshows, Seminars and Events
- ↳ The Welding Library
- ↳ Education Opportunities