Tig welding tips, questions, equipment, applications, instructions, techniques, tig welding machines, troubleshooting tig welding process
Post Reply
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

After a week of TIG practice I feel like I'm finally making some good progress but I know I have much to learn. Looking for some weld critiques and advice, good, bad, and the ugly.
My setup is a Lincoln Square Wave 200 set at 55 amps but I have a little pedal left as I'm welding, need to film the display to see where I'm actually at. 1/16 Tungsten 2% lanthanated, Gas lens, 3/32 70S2 filler, Argon at 15CFH. Metal is 1/16 mild steel working on an outside corner joint.
I think I'm running a bit hot and I should probably be using 1/16 filler which would help with backing off the heat?
IMG_0410.jpg
IMG_0410.jpg (44.07 KiB) Viewed 1815 times
IMG_0412.jpg
IMG_0412.jpg (43.46 KiB) Viewed 1815 times
Mike
  • Posts:
  • Joined:
    Mon Dec 06, 2010 1:09 pm
  • Location:
    Andover, Ohio

Welcome to the forum.
M J Mauer Andover, Ohio

Linoln A/C 225
Everlast PA 200
cj737
  • Posts:
  • Joined:
    Thu Sep 29, 2016 8:59 am

Your amperage setting is probably fine with 1/16" filler, but as you've discovered, the 3/32 is soaking up all the heat you have set available. Either increase your amps to 80 and use less pedal or reduce your wire size to match the amps needed.

Filler causes the pool to chill. You're needing the full heat because of the new material (wire) you're adding to the puddle.

I think most folks set their amps much higher than required, but use the pedal to "feather" the amount of amps being used. This allows more freedom and finer tuning while welding. Backing off the heat as you go becomes normal as the metal soaks up and accumulates the heat.
MFleet
  • Posts:
  • Joined:
    Sat Dec 10, 2016 5:26 am
  • Location:
    Houston, Tx.

Definitely get some 1/16 as it is the recommended size and try both back to back.

One of the things that I had to break myself of was camping out in one spot on the pedal. I'm less concerned of the amperage settings are now and it is generally set to mid-high range of what those welding charts spec. Setting it high combined with some manual pulse drills helped quite a bit. I like the ability to romp on it and get a puddle going quick or unfreezing the puddle from a low amperage re-position. Reading the puddle will tell you how much pedal you need.

I did some experimenting with gas flow on 1/16 and cheap gas lens. It was dropped down to as low as 11CFH with sings of contamination beyond that. Maybe you can find some economy there while working with practice pieces.
Miller 350P w/Python
Miller Syncrowave 250DX - Beaterwave project
Hypertherm Powermax65
Hobby class lathe and milling machine
Juni_1976
  • Posts:
  • Joined:
    Wed Apr 05, 2017 11:12 am
  • Location:
    Brea ,Ca

1/16" and 0.45 is most of what I use, keep practicing keep getting better
Poland308
  • Posts:
  • Joined:
    Thu Sep 10, 2015 8:45 pm
  • Location:
    Iowa

Try running a few passes at70 amps. Don't focus on the start but more on picking up on your travel speed. Then back down on your amps by 3 or 5 at a time till you find a speed that matches your pace. The initial results will be a bit frustrating, but after even just a few passes pushing you out of your comfort zone you will be amazed at the results as you back the amps back down.
I have more questions than answers

Josh
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Thanks for all the advice, I'll try to get some welding in this week and see if my hands can comprehend what I've read
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Feel like I'm slowly getting the hang of things, still can't feed rod very well, just need to practice feeding filler while I'm watching TV. Looks less like fidos butt and slightly more like a TIG weld. All criticism and tips appreciated
Attachments
IMG_20171102_233301757.jpg
IMG_20171102_233301757.jpg (42.7 KiB) Viewed 1485 times
IMG_20171102_233238475_LL.jpg
IMG_20171102_233238475_LL.jpg (52.48 KiB) Viewed 1485 times
IMG_20171102_233225775_LL.jpg
IMG_20171102_233225775_LL.jpg (47.8 KiB) Viewed 1485 times
IMG_20171102_233205195_LL.jpg
IMG_20171102_233205195_LL.jpg (43.62 KiB) Viewed 1485 times
IMG_20171102_233141577_LL.jpg
IMG_20171102_233141577_LL.jpg (47.73 KiB) Viewed 1485 times
IMG_20171102_233114134_LL.jpg
IMG_20171102_233114134_LL.jpg (50.4 KiB) Viewed 1485 times
Poland308
  • Posts:
  • Joined:
    Thu Sep 10, 2015 8:45 pm
  • Location:
    Iowa

Lots of improvement from the first pics to these! Your on the right track. It’s just a matter of practice now. As you progress try to not change more than one thing at a time, IE amps,or rod size, cup size, joint angle, or many other things. This will alow you to see how much or little these changes affect things.
I have more questions than answers

Josh
TheBeardedWelder
  • Posts:
  • Joined:
    Mon Nov 06, 2017 8:42 am
  • Location:
    Massachusetts

Looks like you're getting fast. Just keep practicing the movements. Angle, motion, distance, speed.
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Thanks Poland,
Treated myself to a new helmet, Optrel 2.5 Vegaview with a 2x cheater lens, the difference from my old cheap hood is crazy I was basically welding blind. Here's my first weld with the new hood
Attachments
IMG_20171106_165057118_HDR.jpg
IMG_20171106_165057118_HDR.jpg (45.93 KiB) Viewed 990 times
mpete53
  • Posts:
  • Joined:
    Sun Mar 06, 2016 11:33 am
  • Location:
    New York

I felt the same way when I got a good hood..All of a sudden I could see what everyone was talking about
DanielSD
  • Posts:
  • Joined:
    Wed Nov 08, 2017 10:58 am

Hi, I am Daniel :)
I am new here. :geek:
I am a beginner at welding. :idea:
I hope I will get help on this forum about this.
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Played around with some 1/4" steel today tried fooling around with moving the puddle up and down
Attachments
weave.jpg
weave.jpg (44.47 KiB) Viewed 926 times
weave2.jpg
weave2.jpg (40.93 KiB) Viewed 926 times
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Tried welding some aluminum 1/8" thick, I think it turned out ok considering I've only been at it for about 2 weeks
Attachments
box.jpg
box.jpg (53.42 KiB) Viewed 897 times
box2.jpg
box2.jpg (50.16 KiB) Viewed 897 times
3.jpg
3.jpg (37.15 KiB) Viewed 897 times
4.jpg
4.jpg (36.76 KiB) Viewed 897 times
5.jpg
5.jpg (40.67 KiB) Viewed 897 times
6.jpg
6.jpg (38.83 KiB) Viewed 897 times
User avatar

ProjectGoFast wrote:Tried welding some aluminum 1/8" thick, I think it turned out ok considering I've only been at it for about 2 weeks
Looks good to me
Richard
Website
ProjectGoFast
  • Posts:
  • Joined:
    Sat Sep 09, 2017 10:05 am

Started practicing on some 1/16 stainless slowly getting the hang of it
Attachments
SS 2.jpg
SS 2.jpg (62.12 KiB) Viewed 733 times
SS practice.jpg
SS practice.jpg (48.34 KiB) Viewed 733 times
Post Reply