the welds look ok but do not think that i would post them online till u master at least keeping your weave length the same

well will it be a open butt or will it b a tape test either way u are probably gonna have to pass an ultrasound after visual and neither of witch is phorosity going to cut it keep your nossel close and prob 3/4 of an in stick out on your wire make sure that your gas is turned all the way up and it i...

it seems to me that you just got a clean peice of aluminum this time u could avoid future problems just by cleaning the weld surface of all paint trash and old weld before you start and you will have that outcome everytime

lol sure u dont need to take that thing to the scrap yard

the ruber o rings on the whip itself where it connects to the wirefeeder are real bad for dry rotting and letting air into your sheilding gasses wich will cause the same problems as not getting gas

love it glad there is some mechanics out there wit some imagination

well just all ship yards work with fulx core about every day

what type of pipe and what type of welding are u doing stick tig r mig

well since u dont have but two settings for your heat then you are gonna have to turn down your wire speed till it makes a nice sound with no ratt tat tat

a 7018 1/8 is fine for the welding on the i beam how good of a welder are you cuz if u put a bunch of buble gum on it and pull one of ur prized hotrods r whatever kind of car under it and go to pull the motor and it falls then u just sol since i do not know much about you i am gona say this make sur...

hey so what types of welding have you done
let me know and i may b able to turn u on to some work

what are u welding with mig tig r stick

i have a new test coming up it is a naval gmaw unlimited xray horisonal vert and overhead on alumnium they have tested about sixty people and all but five have busted out does anyone have any tips for me i have welded on alumnium at shipyards for about a year and passed several ut's but gotta say th...